Substrates Specifications:
@ 780 nm | Fused Silica Substrates | ITO-Coated Substrates | Silicon Substrates | Borosilicate Substrates | Microscope Slides |
---|
Material | Fused Silica | Soda Lime w/ ITO | Si Substrates | Borosilicate Sub | Microscope Slides |
Sample Holder | DiLL | DiLL | DiLL | 10 × Ø 30 mm | DiLL |
Refractive index | 1.454 | 1.624 [ITO] 1.518 [soda lime] | 3.710 | 1.517 | 1.518 |
Dimension | [25, 25, 0.7] mm |
Thickness variation | ± 25 µm | Surface finish | DSP | [25, 25, 0.7] mm | [25, 25, 0.725] mm | 30 mm Ø, 170 µm | [22, 75, 1] mm |
Thickness variation | ± 25 µm | ± 60 µm | ± 25 µm | ± 10 µm | ± 100 µm |
Surface finish | DSP | DSP | Polished | DSP | DSP |
Density | 2.2 g/cm3 | 2.5 g/cm3 | 2.3290 |
Density | 2.2 g/cm3 |
|
|
Mohs hardness | 5.3-6.5 | 5-6 | 9-10 |
|
|
Melting point | 1400°C | 1000°C | 3265°C |
|
|
Thermal expansion coefficient | 0.54x10-6 K-1 | 0.937 W/m·K | 2.6 µm/(m·K) |
|
|
Heat conductivity | 1 |
.38 W/(m·K) | 0.937 W/(m·K) | 149 |
Heat conductivity | 1.38 W/(m·K) |
|
|
Compatible w/ Solution Set |
3D SF | Compatible w/ 2PP resin | IP-DIP | 3D SF | 3D MF (3D SF, 2D ML) | 3D LF (3D MF, 3D SF, 2D ML) | 3D SF Oil | 3D SF |
Compatible w/ 2PP resin | IP-DIP | IP-S | IP-Q (IP-S, IP-Dip, AZ resin) | IP-L 780 or IP-G 780 | None, unless coated |
Compatible w/ Objective | 63X | 20x, 25x , 63x | 10x, (20x, 25x, 63x) | 63x | 63x |
Combination & Ref index | -0.058 @ 20°C IP-Dip / -0.025 @ 20°C IP-S | -0.145 @ 20° |
|
|
|
Contrast |
|
|
|
|
|
Cleaning & Prep | O2-plasma & silanization | O2-plasma & silanization | RC1 |
|
|
Indium-Tin Oxide (ITO) Coating Specifications:
ITO | Value |
---|
Film Thickness | 18 nm ± 5 nm |
Film Surface Resistance | 100 - 300 Ω |
Film Transmittance | ≥89% |
Sample Holders available at the CNF
...